Injection molding TPU long glass fiber TPU reinforced thermoplastic urethanes The most suitable processing method of TPU is screw injection molding machine. With a single screw of normal length, a three-stage screw can produce a lot of good plasticized uniform melt. If high plasticizing capacity (production capacity) is required, a longer screw can be used. Injection molding TPU long glass fiber T...

TPU polyurethane elastomer injection molding Injection The most suitable processing method of TPU is screw injection molding machine. With a single thread of normal length, the three-section screw can produce a well-plasticized uniform melt. If high plasticizing capacity is required, TPU LONG GLASS FIBER REINFOCED THERMOPLASTIC requires the use of longer screws. Screws in the short compression zon...

Introducation LFT-G is the product name for long fiber reinforced thermoplastic materials for injection moldings,compression molding and extrusion.Retention of fiber length in the finished part is key to the performance .Fiber length is retained by proper use of free flowing check valves,metering screws and a complete evaluation of the mold to reduce high shear and allow the materials to fill the ...

TPU is usually medium to generally transparent, and some are milky white or turbid. Polyether TPU after adding long glass fiber is much more transparent than polyester TPU. Through the thermal analysis of TPU grades, its performance in various applications can be measured. TPU relies on heat to obtain new shapes during extrusion and injection molding. Since multifunctional TPUs need to be heated r...

Compared with other nylons, PA12 long carbon fiber composite material has low density, good low temperature resistance and wear resistance, has a certain degree of self-lubrication, and its water absorption rate is lower than other nylons. The resistance to stress cracking is better than PA6 and PA66, and it has excellent resistance to alkali, oil and grease. PA12 resin has high crystallinity, low...

What is the TPU material? TPU(Thermoplastic polyurethanes) name is thermoplastic polyurethane elastomer rubber, TPU is a kind of polymer material between rubber and plastic, which is synthesized by reaction polymerization of diphenyl methane diisocyanate (MDI), toluene diisocyanate (TDI) and other diisocyanate molecules with macromolecular polyols and low molecular polyols (chain extender). It has...

Xiamen LFT Composite Plastic Co.,LTD was established in 2009, is a brand-name global suppliers of long fiber reinforced thermoplastic materials integrating product research & development（R&D）, production and sale marketing. Our LFT products have passed the ISO9001&16949 system certification and have obtained lots of national trademarks and patents, covering the fields of automotive, mi...

summaries 9,10-Dihydro-9-oxa-10-phospha-phenanthrene-10-oxide (DOPO) was utilized as a flame retardant for the preparation of mass fraction 20% long glass fiber (LGF) reinforced thermoplastic polyurethane/polybutylene terephthalate/DOPO (20% LGF/TPU/PBT/DOPO) flame retardant composites were prepared, and the flame retardancy, rheological and mechanical properties of the flame retardant composites ...

TPU Introduction Thermoplastic polyurethane elastomer abbreviated as TPU, also known as PU thermoplastic, is a linear block copolymer composed of oligomer polyol soft segment and diisocyanate-chain extender hard segment. TPU molecule contains -NH-COO- groups, many of its characteristics depend on the type of long-chain diols, its hardness with hard segments to do the ratio to adjust its light agin...

(1) Improper control of molding conditions If the injection pressure is too low, the injection and holding time is too short, the injection speed is too slow, the material temperature and mold temperature are too high, the cooling of the plastic part is insufficient, the temperature is too high during demolding, the temperature around the insert is too low, or there is insufficient material supply...

(1) P: Poor flow of the molten material leads to the formation of concentric flow marks resembling growth rings on the surface of injection-molded parts, centered around the gate. When low-temperature, high-viscosity molten material with poor flow performance is injected into the cavity in a semi-cured, fluctuating state through the injection port and runner, the material flows along the cavity su...

Mold temperature too low Cause: If the mold temperature is too low, the melt cools too quickly during flow, causing the glass fibers to not be fully encapsulated by the base resin and float to the surface. Solution: Increase the mold temperature appropriately to ensure the melt has sufficient fluidity to uniformly coat the glass fibers. Regularly check the mold temperature control system to ensure...